ALUMINUM ALLOY FOR DIE CASTING THIN-WALLED PRODUCTS AND ELECTRONIC DEVICE

The present invention provides an aluminum alloy for die casting a thin-walled product, capable of satisfying high liquidity, high toughness, and high corrosion resistance, and an electronic device. According to various embodiments of the present invention, the aluminum alloy for die casting a thin-walled product comprises: greater than or equal to 9.0 to less than or equal to 11.0 wt% of silicon (Si); greater than or equal to 1.0 to less than or equal to 1.3 wt% of magnesium (Mg); greater than or equal to 0.0001 to less than or equal to 0.9 wt% of iron (Fe); greater than or equal to 0.0001 to less than 0.1 wt% of copper (Cu); over 2.0 to less than or equal to 3.0 wt% of zinc (Zn); the amount satisfying a following contained ratio of strontium (Sr); and a residual amount of aluminum (Al). The contained ratio of the strontium (Sr) may be in a range of (wt% of Si - 1.74 X wt% of Mg) : wt% of Sr = 200-1000 : 1. Also, various embodiments are possible. 다양한 실시예에 따르면, 박육 제품 다이캐스팅용 알루미늄 합금은, 상기 합금의 총 중량에 대하여, 9.0 중량% 이상 11.0 중량% 이하의 규소(Si), 1.0 중량% 이상 1.3 중량% 이하의 마그네슘(Mg), 0.0001 중량% 이상 0.9 중량% 이하의 철(Fe), 0.0001 중량% 이상 0.1 중량% 미만의 구리(Cu), 2.0 중량% 초과 3.0 중량% 이하의 아연(Zn), 하기 스트론튬(Sr)의 함유 비율을 충족하는 양의 스트론튬(Sr), 및 잔여량의 알루미늄(Al)을 함유하고, 상기 스트론튬(Sr)의 함유 비율은 (Si의 중량% - 1.74 × Mg의 중량%) : Sr의 중량% = 200~1000 : 1의 범위일 수 있다. 그 밖에 다양한 실시예들이 가능할 수 있다.