Ultra early strength binder and Ultra early strength concrete using the same

The present invention relates to an ultrahigh early strength binder using ultrahigh early strength binder, capable of securing 5MPa which is a required strength for demolding a side mold within 12 hours, and to an ultrahigh early strength concrete composition using the same. The ultrahigh early strength binder of the present invention is a powder composition obtained by mixing calcium sulfo aluminate (CSA) and gypsum, wherein a weight ratio of CaO to SO_3 contained therein is 1 : 1.9 to 2.3, and a weight ratio of Al_2O_3 to SO_3 contained therein is 1 : 0.8 to 1.1. In addition, the concrete composition of the present invention is prepared by mixing a binder, a fine aggregate, a coarse aggregate, and water, wherein the unit binder amount is 330 to 340 kg/m^3, the unit quantity is 170 to 200 kg/m^3, the binder is prepared by 82 to 85 wt% of cement and 15 to 18 wt% of the ultrahigh early strength binder, and the compression strength of the age 12 hours exceeds 5 MPa by satisfying 24 to 40 MPa of the compression strength of the age 28 days and 150 mm or more of slump under condition of in-between seasons of 12 to 13°C of a curing temperature. 본 발명은 12시간 내에 측면 거푸집 탈형 소요강도인 5MPa를 확보할 수 있는 초조강 결합재 및 이를 이용한 초조강 콘크리트 조성물에 관한 것이다. 본 발명은 CSA(Calcium Sulfo Aluminate) 및 석고가 혼합된 분체 조성물로서, 함유된 CaO와 SO의 중량비가 1:1.9~2.3이고, 함유된 AlO와 SO의 중량비가 1:0.8~1.1인 것을 특징으로 하는 초조강 결합재」를 제공한다. 또한, 본 발명은 「결합재, 잔골재, 굵은골재 및 물의 배합으로 조성되는 콘크리트 조성물로서, 단위 결합재량 330~340kg/㎥, 단위 수량 170~200kg/㎥이고, 상기 결합재는 시멘트 82~85wt% 및 제1항의 초조강 결합재 15~18wt%로 조성되고, 양생온도 12~13℃의 간절기 조건에서 재령 28일 압축강도 24~40MPa 및 슬럼프 150mm 이상이 충족되면서, 재령 12시간 압축강도가 5MPa을 초과하는 것을 특징으로 하는 초조강 콘크리트 조성물」을 함께 제공한다.