BONDING TECHNIQUE FOR OVERCOMING THE CRITICAL SIZE OF METALLIC GLASS

The present invention relates to a bonding method capable of producing a bulk amorphous alloy with a size larger than a critical size by bonding amorphous alloys in a bulk state regardless of the number, shape, and the like of the amorphous alloys. The bonding method includes: a preparation step of preparing the amorphous alloy in the bulk state at a size in which the smallest one among a width, a length, and a height is 0.5 mm or greater as a raw material; a heating step of heating at least one between a lower plate and an upper plate of a press device or a specimen based on a glass transition temperature (T_g) and a crystallization starting temperature (T_x) ranging from a temperature of T_g - 0.2 T_g to a temperature lower than T_x; a bonding step of placing the amorphous alloys on the press device and bonding the amorphous alloys by pressing the amorphous alloys while maintaining the heating temperature; and a cooling step of cooling the bonded amorphous alloys. The bonding method of the present invention is capable of forming the amorphous alloys with a size larger than the critical size by bonding the materials regardless of the number, the shape and the like of the amorphous alloys in the bulk state, thereby obtaining an effect of improving the utilization of the amorphous alloys as a structural material. 본 발명은 벌크 상태인 비정질 합금의 개수와 형태 등에 무관하게 재료들을 접합하여 임계 크기를 넘어선 벌크 비정질 합금 재료를 만들 수 있는 접합방법에 관한 것으로, 가로와 세로 및 높이 중에서 가장 작은 값이 0.5 mm 이상인 벌크 상태의 비정질 합금을 원료로 준비하는 준비단계; 상기 비정질 합금의 유리천이온도(T)와 결정화 개시 온도(T)를 기준으로 T-0.2T이상에서 T미만의 온도 범위로 프레스 장치의 하판과 상판 중에 적어도 하나 내지 시편을 가열하는 가열단계; 상기 프레스 장치에 비정질 합금 원료들을 위치하고 가열 온도를 유지하면서 가압하여 상기 비정질 합금 원료들을 서로 접합하는 접합단계; 및 접합된 비정질 합금 재료를 냉각하는 냉각단계를 포함하여 구성된 것을 특징으로 한다. 본 발명의 접합 방법은 벌크 상태인 비정질 합금의 개수와 형태 등에 무관하게 재료들을 접합하여 임계 크기를 넘어선 벌크 비정질 합금 재료를 만들 수 있기 때문에 비정질 합금 재료의 구조재료로 활용성을 높일 수 있는 효과가 있다.