Metal nanowire ink composition or transparent conductive film comprising the same and the preparation method thereof

Provided are a method to prepare a copper nanowire, a copper nanowire prepared thereof, and a method to prepare ink composition and a transparent conductive film. According to the present invention, the method to prepare a copper nanowire comprises: a step of adding a copper chloride, a reducing agent, and a copper capping agent to distilled water to prepare a mixture solution; a step of introducing the mixture solution to an atmospheric pressure reactor or a high pressure reactor to perform a reaction at 80-120C for 6-24 hours to prepare a copper nanowire-formed reaction solution; and a step of cooling and refining the reaction solution to obtain a copper nanowire. Since the copper chloride and distilled water are used; the preparation process is simple and the copper nanowire is able to be prepared at low costs, whereby a highly efficient transparent conductive film is able to be prepared. 구리 나노선의 제조방법, 이에 의해 제조된 구리 나노선, 잉크 조성물 및 투명 전도막의 제조방법이 제공된다. 본 발명에 따른 구리 나노선의 제조방법은 증류수에 염화제이구리, 환원제 및 구리 캡핑제를 첨가하여 혼합 용액을 제조하는 단계; 상기 혼합 용액을 상압 또는 고압 반응기에 넣고 80℃ 내지 120℃ 에서 6시간 내지 24시간 반응시켜 구리 나노선이 형성된 반응용액을 제조하는 단계; 및 상기 반응용액을 냉각 및 정제하여 구리 나노선을 얻는 단계를 포함한다. 염화제이구리 및 증류수를 사용하므로 제조공정이 간단하고 저렴한 제조비용으로 구리 나노선을 제조할 수 있고, 이에 의해 효율이 향상된 투명 전도막을 제조할 수 있다.