HIGH-STRENGTH STEEL PLATE FOR A CAN AND METHOD FOR MANUFACTURING SAID HIGH-STRENGTH STEEL PLATE

A method for manufacturing a high-strength steel sheet for a can, including (a) hot rolling a steel slab at a slab extraction temperature of 1200° C. or more and a finish rolling temperature of (Ar3 transformation temperature−30)° C. or more, the steel slab containing, on the basis of mass percent,...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	ARATANI MAKOTO, SUJITA SHIGEKO, KAWAMURA KATSUHITO, SATO KAKU, KOIZUMI MASAKI, KATO TOSHIKATSU, TANAKA TAKUMI, KOJIMA KATSUMI
Format:	Patent
Sprache:	eng ; kor
Schlagworte:	ALLOYS CHEMISTRY FERROUS OR NON-FERROUS ALLOYS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS PERFORMING OPERATIONS PUNCHING METAL ROLLING OF METAL TRANSPORTING TREATMENT OF ALLOYS OR NON-FERROUS METALS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	A method for manufacturing a high-strength steel sheet for a can, including (a) hot rolling a steel slab at a slab extraction temperature of 1200° C. or more and a finish rolling temperature of (Ar3 transformation temperature−30)° C. or more, the steel slab containing, on the basis of mass percent, more than 0.02%, but 0.10% or less of C, 0.10% or less of Si, 1.5% or less of Mn, 0.20% or less of P, 0.20% or less of S, 0.10% or less of Al, 0.0120% to 0.0250% of N, and the balance being Fe and incidental impurities; (b) coiling at a temperature of 650° C. or less; (c) pickling; (d) carrying out a first cold rolling; (e) continuously annealing; and (f) carrying out a second cold rolling at a reduction ratio of 10% or more and less than 20%.