Heat treatment method of high strength tension steel sheet included perlite

PURPOSE: A method for heat treating high tensile strength steel sheet containing pearlite is provided to obtain the same as or more excellent characteristics compared to dual phase steel by improving existing heat treatment method so that quenching and tempering are not required, and strength after processing is improved. CONSTITUTION: The method comprises the processes of maintaining a dual phase steel used as a high tensile strength steel sheet at temperature of 730 deg.C for two minutes; cooling the dual phase steel to temperature of 400 deg.C at a cooling rate of 0.5 deg.C/sec; and cooling the dual phase steel to an ordinary temperature at a cooling rate of 6 deg.C/sec so that the resulting steel sheet has structure of ferrite, pearlite and martensite for continuously forming yield strength during tension. 본 발명은 퍼얼라이트 조직이 포함된 고장력강판의 열처리 방법에 관한 것으로서, 기존에 2상조직강의 열처리 패턴을 개선하여, 2상조직강내에 퍼얼라이트가 형성되더라도 인장시 불연속항복이 일어나지 않아 조질열처리가 필요없어지고, 성형시 2상조직강보다 가공경화지수가 2배 이상 증가되어 가공후의 강도 향상을 도모할 수 있도록 한 것이다. 이를 위해, 본 발명은 고장력강판으로 사용되고 있는 2상조직강을 730℃에서 2분간 유지한 후, 400℃까지 0.5℃로 냉각한 다음, 6℃/sec속도로 상온까지 냉각시켜, 인장시 연속항복강도를 형성하는 페라이트+퍼얼라이트+마르텐사이트로 조직으로 구성되도록 한 것을 특징으로 하는 퍼얼라이트 조직이 포함된 고장력강판의 열처리 방법을 제공한다.