High Pressure Nitrocarburizing Treatment Method of Cold Press Die for Automobile Parts

PURPOSE: A high pressure nitrocarburizing method of cold press die for automobile parts is provided to substantially reduce time required for forming 0.1 mm of depth of nitride layer, increase 250 Hv or more of surface hardness and improve life time of the die compared to conventional ordinary pressure nitrocarburizing. CONSTITUTION: The high pressure nitrocarburizing method of cold press die for automobile parts is characterized in that carbon steel or alloy steel is nitrocarburized to a temperature of 550 to 590 deg.C for 1 to 3 hours in a mixed gas of ammonia gas, nitrogen gas and carbonic acid gas maintaining a pressure of 5 to 9 kgf/cm¬2 using a pressure resistant nitrocarburizing furnace, wherein the mixed gas comprises 40 wt.% of ammonia gas, 55 wt.% of nitrogen gas and 5 wt.% of carbonic acid gas. 본 발명에 따르면, 탄소강 또는 합금강을 내압 연질화로를 이용하여 압력 5~9kgf/cm을 유지하는 암모니아가스＋질소가스＋탄산가스의 혼합가스에서 550~590℃의 온도로 1~3시간 연질화 처리하는 것을 특징으로 하는 자동차부품 제조용 냉간프레스 금형의 고압 연질화 처리방법이 제공된다. 본 발명에 따른 고압 연질화처리 방법은 종래의 상압 연질화처리 방법보다 연질화 효과를 극대화하여 질화층깊이 0.1mm를 형성시키는데 소요되는 시간을 종래보다 훨씬 단축시키며, 표면경도도 상압 연질화처리 방법보다 250Hv 이상 높일 수 있다. 또한 질화층에 균열이 발생하지 않아 금형의 수명이 향상된다.