Method of manufacturing Copper bearing steel wire for pre-stressed concrete

PURPOSE: A method of manufacturing copper bearing steel wire for pre-stressed concrete (PC steel), which is characterized in that lamellar gap between lamellar pearlite is refined by adding Cu to high carbon wire rod steel and hardening is caused by Cu when bluing treatment is performed after drawing. CONSTITUTION: The method includes the steps of reheating a steel billet comprising C 0.80 to 1.42 wt.%, Si 0.15 to 0.35 wt.%, Mn 0.60 to 0.90 wt.%, 0.025 wt.% or less of P, 0.025 wt.% or less of S, Cu 0.2 to 4.0 wt.%, a balance of Fe and incidental impurities in temperature range of 1000 to 1200°C; hot rolling the steel billet into wire rod, wherein FDT (finish delivery temperature) is 950 to 1200°C; water-cooling the wire rod to 800-850°C, followed by coiling; cooling the wire rod at a cooling rate of 3 to 20°C/sec; drawing the wire rod; and heat treating the drawn wire rod at 250 to 450°C for 30 to 60 sec. 본 발명은 콘크리트 보강용 강선(이하 PC강선, Prestressed Concrete)용으로 사용되는 선재에 관한 것으로, 그 목적은 고탄소강 선재에 Cu를 첨가하여 펄라이트 층상간격을 미세화시키고, 신선가공한 다음에 블루잉(Bluing)열처리할 때 Cu에 의해 시효경화되는 PC강선용 선재의 제조방법을 제공하는 것이다. 상기 목적을 달성하기 위한 본 발명은, 중량%로, C: 0.80-1.42%, Si: 0.15-0.35%, Mn: 0.60-0.90%, P: 0.025%이하, S: 0.025% 이하, Cu: 0.2~4.0%, 나머지 Fe와 기타 불가피하게 함유되는 불순물로 조성되는 빌렛을 1000~1200℃에서 재가열하여 마무리압연온도 950~1200 ℃의 조건으로 열간선재압연하고, 800~850℃까지 수냉하여 권취하는 단계, 권취된 선재를 3~20℃/sec로 냉각하는 단계, 냉각된 선재를 냉간에서 신선가공하고, 이어서 250 ~ 450℃ 온도에서 30초이상 60초 이하 동안 열처리에 의하여 경화하는 단계를 포함하여 이루어지는 Cu함유 고강도 콘크리트 보강용 선재의 제조방법에 관한 것을 그 기술요지로 한다.