HEAT-TREATMENT METHOD FOR IMPROVING THE WEAR-RESISTANCE OF OVERLAY-WELDED NICKEL ALLOY LAYER

PURPOSE: A heat treatment method for improving wear resistance of overlay welded nickel alloy layer is provided to improve hardness and wear resistance of the overlay welded layer by furnace cooling the alloy layer after heat treating the alloy layer for a time impressed according to thickness of a nickel alloy layer overlay welded on a base metal. CONSTITUTION: In a method for improving hardness and wear resistance of a nickel based alloy overlay welded onto a base metal by plasma transferred arc welding, the heat treatment method for improving wear resistance of overlay welded nickel alloy layer comprises the process of furnace cooling the heat treated alloy layer after heat treating the alloy layer at 760 deg.C for a time impressed according to thickness of a nickel based alloy layer overlay welded on a base metal, wherein the heat treatment time impressed according to thickness of the nickel based alloy layer overlay welded on the base metal is one hour per 3 mm thickness of the nickel based alloy layer. 본 발명은 소지금속의 내마모성 향상을 위하여 플라즈마 분말 육성용접(PTAW; Plasma Transferred Arc Welding) 방법으로 소지금속에 형성된 니켈합금 육성용접층의 내마모성 향상을 위한 열처리 방법이다. 이를 위하여, 본 발명은 소지금속인 모재 위에 육성용접된 니켈계 합금층의 두께에 따라 인가된 시간 동안 760℃에서 열처리하여 노냉하는 것을 특징으로 하는 니켈합금 육성 용접층의 내마모성 향상을 위한 열처리 방법을 제공하며, 또한, 상기 육성용접된 니켈계 합금층의 두께에 따라 인가되는 열처리시간은 니켈계 합금층의 두께 3㎜당 1시간인 것을 특징으로 하는 니켈합금 육성 용접층의 내마모성 향상을 위한 열처리 방법을 제공한다. 이와 같이, 본 발명은 모재에 플라즈마 분말 육성용접 방법으로 니켈계 육성용접층을 적층하여 760℃에서 육성용접층의 두께에 따라 인가된 시간동안 열처리를 실시함으로써 마모특성이 우수한 육성층을 얻을 수 있는 효과가 있다.