Urethane modified epoxy resin composition with improved adhesion and flexibility and construction method of thin polmer surface treatment pavement using the same

The present invention relates to a urethane-modified epoxy resin composition with improved adhesion and flexibility and a method for packaging a thin polymer layer containing the same. The urethane-modified epoxy resin composition comprises a base material and an epoxy curing agent, wherein the base material contains bisphenol A diglycidyl ether, polyether-epoxide polymer, polyethylene phenyl polyisocyanate, (((2-ethylhexyl)oxy)methyl)oxirane, aliphatic epoxy resin, and a phosphorus-based antioxidant. According to the present invention, the service life of a concrete surface can be extended. 본 발명은 주제 40 내지 80 중량%와, 에폭시 경화제 20 내지 60 중량%를 포함하는 우레탄 변성 에폭시 수지 조성물로; 상기 주제는 비스페놀 A 디글리시딜 에테르 100 중량부, 폴리에테르-에폭사이드 중합체 10 내지 40 중량부, 폴리에틸렌 페닐 폴리이소시아네이트 1 내지 20 중량부, (((2-에틸헥실)옥시)메틸)옥시란[(((2-Ethylhexyl)oxy)methyl)oxyrane] 1 내지 20 중량부, 지방족 에폭시 수지 1 내지 20 중량부 및 인계 산화방지제 1 내지 20 중량부를 함유하고; 상기 에폭시 경화제는 카르다놀(cardanol) 100 중량부, 3-아미노메틸-3,5,5-트리메틸시클로헥실아민 10 내지 50 중량부, 2,4,6-트리스[(디메틸아미노)메틸]페놀 10 내지 30 중량부, 1-아미노피롤리딘 1 내지 10 중량부, 1-아미노-N-메틸 피페라진 1 내지 10 중량부, 및 아민계 폴리부타디엔 1 내지 10 중량부를 함유하며; 상기 우레탄 변성 에폭시 수지 조성물은 인장강도가 7.6 내지 34.5 MPa이고, 인장신율 30 내지 80 %이며, 압축탄성계수 895 MPa 이하인 것을 사용함으로써, 환경친화적이고, 콘크리트 면과의 부착성 및 인장강도와 신율이 우수하고, 노화 및/또는 박리가 쉽게 발생하지 않아 콘크리트 면의 수명이 연장되며, 내마모성이 우수한 골재를 사용으로 장기 공용 후에도 미끄럼저항성을 확보할 수 있고, 저온에서도 시공이 가능한 부착성 및 유연성이 향상된 우레탄 변성 에폭시 수지 조성물 및 이를 함유하는 폴리머 박층 포장방법에 관한 것이다.