Polymer manufacturing method for producing polyethylene homopolymer or polyethylene vinyl acetate copolymer

The present invention relates to a manufacturing method of a polyethylene or a polyethylene vinyl acetate copolymer. More specifically, the present invention relates to the manufacturing method of a low density polyethylene or a polyethylene vinyl acetate copolymer by a high pressure radical polymerization process in a tubular reactor, wherein the method for polymerization by co-injection of an antioxidant as an additive with a monomer. According to the manufacturing method, it is possible to reduce fouling of walls of a high-pressure separator and a low-pressure separator, and thus manufactured polyethylene or polyethylene vinyl acetate copolymer resin can significantly reduce an insoluble crosslinked gel having a shape factor of less than 2 in a final product. 본 발명은 폴리에틸렌 또는 폴리에틸렌비닐아세테이트 공중합체의 제조방법에 관한 것으로, 더욱 상세하게는 관형반응기에서 고압 라디칼 중합법에 의해 저밀도 폴리에틸렌 또는 폴리에틸렌 비닐 아세테이트 공중합체를 제조하는 방법에 관한 것으로서, 첨가제인 산화방지제를 단량체와 동시 주입하여 중합하는 방법에 관한 것이다. 이 제조 방법에 의하면 고압 분리기 및 저압 분리기 벽면의 파울링을 감소시킬 수 있으며, 제조한 폴리에틸렌 또는 폴리에틸렌 비닐아세테이트 공중합체 수지는 최종 제품 내 형상계수가 2 미만인 불용성 가교겔을 현격히 감소시킬 수 있다.