METHOD FOR PRODUCING CERAMIC COMPOSITION FOR COATING CERAMIC COMPOSITION BY THE METHOD AND COATING MEHTOD USING BY IT

The present invention relates to a method for manufacturing a ceramic coating composition having excellent acid resistance, the coating composition, and a coating method using the same. The method for manufacturing the ceramic coating composition having the excellent acid resistance comprises: a step of mixing 10-40 wt% of dolomite, 0.1-5 wt% of copper oxide, 1-10 wt% of wollastonite, 1-40 wt% of kaolin, 1-30 wt% of a corner stone, 2-30 wt% of borax, and 0.1-5 wt% of cobalt; a step of melting the mixed composition at 1,200-1,600°C to produce an amorphous sintered body; a step of cooling the produced amorphous sintered body; a step of pulverizing the cooling product; a step of coating the pulverized product on a surface of a metal base material; a step of sintering the metal base material on which the composition is coated at the temperature of 800-900°C for 1-20 minutes; and a step of cooling the sintered metal base material. The present invention can form a ceramic thin film which has the excellent acid resistance and is resistant to chemical erosion on the surface of the metal base material without using an organic binder or a high-temperature sintering process. 본 발명은 내산성이 우수한 세라믹 코팅 조성물의 제조방법, 그 코팅 조성물 및 이를 이용한 코팅방법에 관한 것으로, 더 상세하게는 백운석 10~40중량%, 산화구리 0.1~5중량%, 규회석 1~10중량%, 카오린 1~40중량%, 초석 1~30중량%, 붕사 2~30중량%, 코발트 0.1~5중량%를 혼합하는 단계와, 상기 혼합된 혼합물을 1,200~1,600℃로 용융처리하여 비정질 소결체로 제조하는 단계와, 상기 제조된 비정질 소결체를 냉각하는 단계와, 상기 냉각된 냉각물을 분쇄하는 단계와, 상기 분쇄물을 금속 모재의 표면에 도포하는 단계와, 상기 조성물이 도포된 금속 모재를 800~900℃의 온도로 1~20분간 소성처리하는 단계와, 상기 소성처리된 금속 모재를 냉각하는 단계를 포함하는 것을 특징으로 한다. 본 발명에 의하면, 유기바인더의 사용이나 고온 소결의 공정 없이 금속 모재의 표면에 내산성이 우수한, 즉 화학적 침식에 강한 세라믹 박막을 형성시킬 수 있다는 장점이 있다.