FABRICATION METHOD OF SUPERHYDROPHOBIC FILM AND THE SUPERHYDROPHOBIC FILM THEREBY

Provided is a method for manufacturing a superhydrophobic thin film, comprising the following steps: preparing a mold on which a pattern is formed (step 1); forming a polymer layer by coating a polymer solution containing poly(perfluoroalkyl methacrylate) or poly(perfluoroalkyl acrylate) on the mold prepared at the step 1 (step 2); and forming a polymer pattern by bring the mold coated with the polymer solution at the step 2 into contact with a substrate so as to transfer the polymer layer (step 3). The method for manufacturing a superhydrophobic thin film in accordance with the present invention facilitates the manufacture of a superhydrophobic thin film using a micro-contact printing technology, thereby being able to manufacture a superhydrophobic thin film in less time with lower costs than the conventional technique. In addition, a fluorine-based polymer is used, thereby enabling formation of the pattern without surface treatment and printing at room temperature. The superhydrophobic thin film in accordance with the present invention has: an excellent anti-corrosive effect in the case of being formed on a metal substrate; and excellent transmittance in the case of being formed on a transparent substrate. 본 발명은 패턴이 형성된 몰드를 준비하는 단계(단계 1); 상기 단계 1에서 준비된 몰드에 폴리(퍼플루오로알킬 메타크릴레이트)(Poly(perfluoroalkyl methacrylate) 또는 폴리(퍼플루오로알킬 아크릴레이트)(Poly(perfluoroalkyl acrylate)를 포함하는 고분자 용액을 도포하여 고분자 층을 형성하는 단계(단계 2); 및 상기 단계 2에서 고분자 용액이 도포된 몰드를 기판에 접촉시켜 고분자 층을 전사하여 고분자 패턴을 형성하는 단계(단계 3);를 포함하는 초소수성 박막의 제조방법을 제공한다. 본 발명에 따른 초소수성 박막의 제조방법은 미세 인쇄 접촉 기술을 이용하여 간단하게 초소수성 박막을 제조함으로써, 종래 기술에 비하여 매우 빠른 시간에 저비용으로 초소수성 박막을 제조할 수 있는 효과가 있다. 또한, 플루오르계 고분자를 사용하여 표면 처리 없이 패턴을 형성할 수 있고, 상온에서 인쇄가 가능하다.본 발명에 따른 초소수성 박막은 금속 기판에 형성되었을 경우 우수한 부식 방지 효과가 있으며, 투명 기판에 형성되었을 경우 우수한 투과도를 나타낼 수 있다.