METHOD FOR MANUFACTURING SOLID ELECTROLYTE COMPOSITION FOR LITHIUM SECONDARY BATTERY AND THE SAME

The present invention relates to a method for preparing a solid electrolyte composition for a glass-type lithium secondary battery. The present invention minimizes defects and cracks causing reduction of resistance on an interface generated in a solid electrolyte heat treatment process and increases the crystallinity to have enhanced lithium ion conductivity in order to increase ion conductivity lower than that of a liquid electrolyte and improve the state of the interface between the solid electrolyte and an electrode material. The method includes the steps of: (a) mixing raw materials including Li_2O, SiO_2, TiO_2, P_2O_5, BaO, Cs_2O, and V_2O_5; (b) melting the mixed raw materials; (c) rapidly cooling and compressing the melted raw materials at room temperature to prepare electrolyte glass in the set thickness; and (d) elevating the temperature of the electrolyte glass to the set temperature to remove the stress in the set temperature range; and (e) heating the electrolyte glass at higher temperature than the previous step to crystallize the electrolyte glass. 본 발명은 액체 전해질에 비해 낮은 이온 전도성을 높이고 고체 전해질과 전극재료 간에 접촉되는 계면 상태를 향상시키기 위해, 고체 전해질 열처리 과정에서 발생되는 계면에서의 저항을 낮추는 요인이 되는 기공(defect) 및 크랙(crack)을 최소화하고, 결정성을 증대시켜 향상된 리튬 이온 전도성(Li ion conductivity)을 갖는 유리 타입(glass type)의 리튬 이차전지용 고체 전해질 조성물을 제조하는 방법에 관한 것으로, 본 발명에 따른 리튬 이차전지용 고체 전해질 조성물의 제조 방법은, (a) LiO, SiO, TiO, PO, BaO, CsO, VO를 포함하는 재료를 혼합하는 단계; (b) 상기 혼합된 재료를 용융하는 단계; (c) 상기 용융된 재료를 상온에서 급냉하고, 압축하여 설정된 두께의 전해질 유리로 제작하는 단계; (d) 상기 전해질 유리를 설정된 온도로 승온하여 설정된 온도범위에서 응력을 제거하는 단계; 그리고, (e) 상기 전해질 유리를 설정된 온도로 승온하여 상기 응력을 제거하는 단계에서보다 높은 온도범위에서 가열하여 결정화하는 단계;를 포함하는 것을 특징으로 한다.