GLASS-CERAMIC HAVING SPECIFIC THERMAL EXPANSION CHARACTERISTICS

To provide a glass-ceramic improved in thermal expansion behavior, and the use thereof in a precision component.SOLUTION: An LAS glass-ceramic has an average coefficient of thermal expansion CTE at 0-50°C of at most 0±0.1×10-6/K and a thermal hysteresis at least in the temperature range from 15°C to 35°C of less than 0.1 ppm. The LAS glass-ceramic contains following components (in units of mol% based on oxide): SiO2 of 60 to less than 70; Li2O of 7 to 9.6; MgO+ZnO of more than 0.5 to 1.5; R2O of more than 0.5, where R2O may be Na2O and/or K2O and/or Cs2O and/or Rb2O; and also contains a nucleating agent with a content of 1.5 to 6 mol%, where the nucleating agent is at least one component selected from the group consisting of TiO2, ZrO2, Ta2O5, Nb2O5, SnO2, MoO3, WO3, and HfO2.SELECTED DRAWING: Figure 10 【課題】熱膨張挙動が改善されたガラスセラミックスおよび精密部品におけるその使用を提供する。【解決手段】ＬＡＳガラスセラミックスであって、０～５０℃の平均熱膨張係数ＣＴＥが最大で０±０．１×１０－６／Ｋであり、かつ少なくとも１５℃～３５℃の温度範囲でのサーマルヒステリシスが０．１ｐｐｍ未満であり、かつ（酸化物ベースでのモル％単位で）以下の成分、ＳｉＯ２：６０～＜７０、Ｌｉ２Ｏ：７～９．６、ＭｇＯ＋ＺｎＯ：＞０．５～１．５、Ｒ２Ｏ：＞０．５、ここで、Ｒ２Ｏは、Ｎａ２Ｏおよび／またはＫ２Ｏおよび／またはＣｓ２Ｏおよび／またはＲｂ２Ｏであってよいものとする、核生成剤：１．５～６モル％の含有量、ここで、核生成剤は、ＴｉＯ２、ＺｒＯ２、Ｔａ２Ｏ５、Ｎｂ２Ｏ５、ＳｎＯ２、ＭｏＯ３、ＷＯ３、ＨｆＯ２からなる群から選択される少なくとも１つの成分であるものとする、を含む、ＬＡＳガラスセラミックス。【選択図】図１０