METHOD FOR PRODUCING POLYBUTYLENE TEREPHTHALATE RESIN

To provide a polybutylene terephthalate resin which reduces foaming in esterification reaction, improves polymerization speed, and thereby reduces dielectric loss tangent and a foreign matter amount while achieving both production speed and a yield.SOLUTION: A method for producing polybutylene terephthalate includes a step (esterification step) of esterifying a dicarboxylic acid component containing a terephthalic acid as a main component and a diol component containing butane diol as a main component, and a step (polycondensation step) of subjecting a product produced in the esterification step to polycondensation, wherein in the esterification step, a charged molar ratio ((B)/(A)) of the butane diol (B) to the terephthalic acid (A) is controlled to be 1.6 to 2.0, 0.1 to 2.0 mol% of aliphatic alcohol (C) having 10 to 50 carbon atoms is added to 100 mol% of the terephthalic acid and the esterification reaction is performed, and peripheral speed of a stirring blade of the reaction tank is controlled to be the range of 2.0-4.0 m/s.SELECTED DRAWING: None 【課題】エステル化反応時の発泡を低減し、重合速度を高めることで、生産速度と収率を両立しつつ、さらに誘電正接や異物量が低減されたポリブチレンテレフタレート樹脂を得る。【解決手段】テレフタル酸を主成分とするジカルボン酸成分と、ブタンジオールを主成分とするジオール成分とをエステル化する工程（エステル化工程）、その後、該エステル化工程で生成された生成物を重縮合する工程（重縮合工程）を有するポリブチレンテレフタレートの製造方法であって、前記エステル化工程において、テレフタル酸（Ａ）とブタンジオール（Ｂ）の仕込みモル比（（Ｂ）／（Ａ））を１．６～２．０とし、かつ、炭素数が１０以上５０以下の脂肪族アルコール（Ｃ）をテレフタル酸１００ｍｏｌ％に対して０．１～２．０ｍｏｌ％添加してエステル化反応を行い、かつ、反応槽の攪拌翼の周速度を２．０ｍ／ｓ～４．０ｍ／ｓの範囲とする。【選択図】 なし