THERMOPLASTIC ELASTOMER COMPOSITION, INJECTION MOLDING, AND AIR BAG STORAGE COVER

To provide a thermoplastic elastomer composition which enables excellent molding that is excellent in designability while maintaining low temperature impact resistance.SOLUTION: A thermoplastic elastomer composition contains the following components (A) to (C), wherein a die swell ratio (test temperature 210°C, and shear rate of 243/s) in capillary rheometer (JIS K 7199) is 1.10 or more, glossiness when a test piece for glossiness measurement composed of the thermoplastic elastomer composition is measured at an incident angle of 60° according to ISO 2813 is 50% or less, and a bending modulus of elasticity when a test piece for bending modulus of elasticity measurement composed of the thermoplastic elastomer composition is measured according to ISO 178 (2010) is 100-700 MPa. Component (A): propylene-based block copolymer, component (B): ethylene-α-olefin copolymer having α-olefin having 4 or more carbon atoms, and component (C): ethylene-propylene-non-conjugated diene copolymer.SELECTED DRAWING: None 【課題】低温耐衝撃性を維持しながら、意匠性に優れた成形品を可能とする熱可塑性エラストマー組成物を提供する。【解決手段】下記成分（Ａ）～（Ｃ）を含有する熱可塑性エラストマー組成物であって、キャピラリーレオメーター（ＪＩＳ Ｋ７１９９）におけるダイスウェル比（試験温度２１０℃、せん断速度２４３／ｓ）が１．１０以上であり、該熱可塑性エラストマー組成物よりなる光沢測定用試験片についてＩＳＯ ２８１３に従って入射角６０°で測定した光沢度が５０％以下であり、かつ該熱可塑性エラストマー組成物よりなる曲げ弾性率測定用試験片についてＩＳＯ １７８（２０１０年）に従って測定した曲げ弾性率が１００～７００ＭＰａである、熱可塑性エラストマー組成物。成分（Ａ）：プロピレン系ブロック共重合体成分（Ｂ）：α－オレフィンの炭素数が４以上であるエチレン・α－オレフィン共重合体成分（Ｃ）：エチレン・プロピレン・非共役ジエン共重合体【選択図】なし