FERRITIC STAINLESS STEEL WELDING STRUCTURE

To provide a ferritic stainless steel welding structure that is excellent in high-temperature oxidation resistance, corrosion resistance and dimensional accuracy.SOLUTION: A ferritic stainless steel welding structure contains a base material and a weld metal part. The base material contains, in mass, C: 0.050% or less, Mn: 1.00% or less, Ni: 1.00% or less, P: 0.100% or less, S: 0.050% or less, Cr: 10.00 to 24.00%, N: 0.050% or less, Cu: 1.00% or less, Mo: 1.00% or less, Si: 3.00% or less, Al: 0.80 to 5.00%, Nb: 0.50% or less, Ti: 0.50% or less, with the total content of Nb and Ti being 6(C+N) or more (C and N denoting the content of C and N respectively), and with the balance being Fe and impurities. The base material has an average crystal orientation difference of 0.15° or more. In the weld metal part, the grain boundary C level is 10 mass% or more. The ferritic stainless steel welding structure has an oxide film containing Al of 30 mass% or more on its surface.SELECTED DRAWING: None 【課題】耐高温酸化性、耐食性及び寸法精度に優れるフェライト系ステンレス鋼溶接構造体を提供する。【解決手段】母材及び溶接金属部を含むフェライト系ステンレス鋼溶接構造体である。母材は、質量基準で、Ｃ：０．０５０％以下、Ｍｎ：１．００％以下、Ｎｉ：１．００％以下、Ｐ：０．１００％以下、Ｓ：０．０５０％以下、Ｃｒ：１０．００～２４．００％、Ｎ：０．０５０％以下、Ｃｕ：１．００％以下、Ｍｏ：１．００％以下、Ｓｉ：３．００％以下、Ａｌ：０．８０～５．００％、Ｎｂ：０．５０％以下、Ｔｉ：０．５０％以下を含み、Ｎｂ及びＴｉの合計含有量が６（Ｃ＋Ｎ）以上（Ｃ及びＮは、Ｃ及びＮの含有量をそれぞれ表す）であり、残部がＦｅ及び不純物からなる組成を有する。母材は、平均結晶方位差が０．１５°以上である。溶接金属部は、粒界Ｃｒ濃度が１０質量％以上である。フェライト系ステンレス鋼溶接構造体は、Ａｌを３０質量％以上含む酸化皮膜を表面に備える。【選択図】なし