DIBUTYLENE GLYCOL CO-POLYMERIZED POLYBUTYLENE TEREPHTHALATE PELLET AND MANUFACTURING METHOD THEREOF, AND MOLDING AND MANUFACTURING METHOD THEREOF

To provide a dibutylene glycol co-polymerized polybutylene terephthalate pellet with less color tone increase in drying under air, and capable of suppressing contamination of a chill roll, etc., when fabrication, etc. are applied for making into a film.SOLUTION: A dibutylene glycol co-polymerization polybutylene terephthalate pellet is a pellet of a dibutylene glycol co-polymerized polybutylene terephthalate including a unit derived from a dicarboxylic acid component having a terephthalic acid component as a primary component and a unit derived from a diol component containing dibutylene glycol and having 1,4-butanediol as a primary component. A ratio of the unit derived from dibutylene glycol to the unit derived from a dicarboxylic acid component is 0.05 to 1.0 mol%. A difference in intrinsic viscosity between a center part and a surface layer part of the pellet is over 0.03dL/g.SELECTED DRAWING: Figure 1 【課題】空気下での乾燥時の色調増加が少なく、フィルム化のための成形加工等をした場合に、冷却ロール等の汚染が抑制されるジブチレングリコール共重合ポリブチレンテレフタレートペレットを提供する。【解決手段】テレフタル酸成分を主成分とするジカルボン酸成分に由来するユニットと、１，４－ブタンジオールを主成分とし、ジブチレングリコールを含むジオール成分に由来するユニットとからなるジブチレングリコール共重合ポリブチレンテレフタレートのペレットであって、前記ジカルボン酸成分に由来するユニットに対するジブチレングリコールに由来するユニットの割合が０．０５～１．０モル％であり、前記ペレットの中心部と表層部の固有粘度の差が０．０３ｄＬ／ｇを超えることを特徴とするジブチレングリコール共重合ポリブチレンテレフタレートペレット。【選択図】図１