RESIN COMPOSITION, CROSSLINKED RESIN COMPOSITION AND MOLDED BODY

To provide a composition capable of suppressing blocking of a 4-methyl-1-pentene polymer and suppressing bleeding of a crosslinking auxiliary as a composition comprising a 4-methyl-1-pentene polymer and a crosslinking auxiliary.SOLUTION: There is provided a resin composition (X1) comprising 100 pts.mass of a 4-methyl-1-pentene polymer (A) satisfying the following requirements (A-a) to (A-c) and 0.1 to 50 pts.mass of a crosslinking auxiliary (B): (A-a) the content ratio of a constitutional unit (U1) derived from 4-methyl-1-pentene is 80 to 100 mol% and the content ratio of a constitutional unit (U2) derived from an α-olefin having 2 to 20 carbon atoms (excluding 4-methyl-1-pentene) is 0 to 20 mol% (provided that the total content ratio of the constitutional unit (U1) and the constitutional unit (U2) is defined as 100 mol%); (A-b) the melt flow rare (MFR) under a load of 5 kg at 260°C is in the range of 0.01 to 250 g/10 min; (A-c) the melting point measured by DSC is in the range of 200 to 250°C.SELECTED DRAWING: None 【課題】本発明は、４－メチル－１－ペンテン重合体と架橋助剤とを含む組成物として、４－メチル－１－ペンテン重合体のブロッキングを抑制でき、架橋助剤のブリードも抑制できる組成物を提供することを目的とする。【解決手段】下記要件（Ａ－ａ）～（Ａ－ｃ）を満たす４－メチル－１－ペンテン重合体（Ａ）１００質量部と、架橋助剤（Ｂ）０．１～５０質量部とを含む樹脂組成物（Ｘ１）：（Ａ－ａ）４－メチル－１－ペンテンから導かれる構成単位（Ｕ１）の含有率が８０～１００モル％であり、炭素原子数２～２０のα－オレフィン（４－メチル－１－ペンテンを除く。）から導かれる構成単位（Ｕ２）の含有率が０～２０モル％〔但し、（構成単位（Ｕ１）および構成単位（Ｕ２）の含有率の合計を１００モル％とする。）である；（Ａ－ｂ）２６０℃、５ｋｇ荷重下のメルトフローレート（ＭＦＲ）が０．０１～２５０ｇ／１０分の範囲にある；（Ａ－ｃ）ＤＳＣで測定した融点（Ｔｍ）が２００～２５０℃の範囲にある。【選択図】なし