POLYMER-BOUND CERAMIC PARTICLE BATTERY SEPARATOR COATING

To provide a method for manufacturing an electrochemical device which includes a separator that does not form cracks or cause short circuits due to shrinkage when an electrochemical cell is either heated or compressed.SOLUTION: A method for forming an electrochemical device includes: a step 101 of mixing a ceramic particulate material with a curable binder mixture to form a slurry; a step 102 of applying the slurry to a separator to form a slurry coated separator; and a step 104 of subjecting the slurry coated separator to UV or EB curing, the ceramic particulate material being distributed throughout a porous nonionic cured matrix and present in an amount of from 85 to about 98 weight percent based on the total weight of the porous nonionic cured matrix. The porous nonionic UV or EB cured matrix maintains its shape and does not melt, at 100°C.SELECTED DRAWING: Figure 3 【課題】電気化学セルが、加熱されるか、または圧縮される場合、収縮に起因して、亀裂を形成せず、また短絡も引き起こさないセパレーターを備えた電気化学デバイスの製造方法を提供する。【解決手段】セラミック粒子材料及び硬化性結合剤混合物と混合してスラリーを形成するステップ１０１と、スラリーをセパレーターに塗布してスラリーでコーティングされたセパレーターを形成するステップ１０２と、スラリーでコーティングされたセパレーターをＵＶ硬化またはＥＢ硬化、セラミック粒子材料は前記多孔性の非イオン性硬化マトリックス全体にわたって分配されるとともに、多孔性の非イオン性硬化マトリックスの総重量の８５から９８パーセントの量存在するステップ１０４と、を含み、前記多孔性の非イオン性ＵＶまたはＥＢ硬化マトリックスは、１００℃においてその形状を維持し、融解しない、電気化学デバイスを形成する方法である。【選択図】図３