COLORED GLASS WITH HARD COAT LAYER

To reduce occurrence of cracks in a hard coat layer in a colored glass with the hard coat layer formed using an organic glass substrate as a substrate.SOLUTION: Colored glass 10 with a hard coat layer is provided that comprises an organic glass substrate 4 and a hard coat layer 1, the organic glass substrate 4 is a single layer constitution composed of a single colored layer or a multi-layer constitution in which at least one outermost surface layer is a colored layer, the organic glass substrate 4 having infrared transmittance at a wavelength of 800 nm or more and 1,000 nm or less of 70% or less, the hard coat layer 1 includes a curable resin as a main material resin and is layered on the surface of the colored layer of the organic glass substrate 4 through an intermediate resin substrate layer 3, the intermediate resin substrate layer 3 has a glass transition temperature (Tg) of 63°C or higher, a thickness of 50 μm or more and infrared transmittance at a wavelength of 800 nm or more and 1,000 nm or less of 80% or more.SELECTED DRAWING: Figure 1 【課題】基材として有機ガラス基材を用いるハードコート層付き有色ガラスにおいて、ハードコート層のクラックの発生を低減させること。【解決手段】有機ガラス基材４と、ハードコート層１と、を備えるハードコート層付き有色ガラス１０であって、有機ガラス基材４は、単一の有色層からなる単層構成であるか、又は、少なくとも一方の最表面層が有色層である多層構成であって、波長８００ｎｍ以上１０００ｎｍ以下における赤外線透過率が７０％以下であり、ハードコート層１は、硬化性樹脂を主たる材料樹脂とし、有機ガラス基材４の有色層の表面に、中間樹脂基材層３を介して、積層されていて、中間樹脂基材層３は、ガラス転移温度（Ｔｇ）が６３℃以上であり、厚さが５０μｍ以上であって、波長８００ｎｍ以上１０００ｎｍ以下における赤外線透過率が８０％以上である、ハードコート層付き有色ガラス１０とする。【選択図】図１