SEAL MATERIAL AND SEAL STRUCTURE

To provide a seal material revealing excellent sealability when applied to repair of a high temperature device.SOLUTION: A seal structure 100 has what repairs a degraded seal member 42, a first component and a second component. The first component is at least one metal salt selected from a group composed of silicate alkali metal salt, silicate alkaline earth metal salt, ortho phosphoric acid alkali metal salt, and ortho phosphoric acid alkaline earth metal salt. The second component includes particles of oxide that has fine grains whose average particle diameter is 10 μm or less and coarse grains whose average particle diameter ranges from 200 μm to 1000 μm. The fine grains are included within the range of 8 mass % and 45 mass % with respect to a total mass of the coarse grains and the fine grains. A total of metal salt silicate components and phosphoric acid components with respect to a sum of alkali metal components and alkaline earth metal components included in the first component on the oxide basis ranges from 1.5 to 3.5 at a molar ratio, and mass ratio of the first component with respect to the second component is within the range from 0.35 to 0.9.SELECTED DRAWING: Figure 1 【課題】高温装置の補修に適用した際に良好なシール性を発揮するシール材を提供する。【解決手段】シール構造体１００は、劣化したシール部材４２を補修するもの、第１の成分と、第２の成分と、を有し、第１の成分は、ケイ酸アルカリ金属塩、ケイ酸アルカリ土類金属塩、オルトリン酸アルカリ金属塩、オルトリン酸アルカリ土類金属塩からなる群から選定される少なくとも一つの金属塩であり、第２の成分は、平均粒子径が１０μｍ以下の細粒と、平均粒子径が２００μｍ〜１０００μｍの粗粒とを有する酸化物の粒子を含み、細粒は、粗粒と細粒の合計質量に対して、８質量％〜４５質量％の範囲で含まれ、第１の成分に含まれるアルカリ金属成分とアルカリ土類金属成分の酸化物基準の合計に対する、金属塩のケイ酸成分とリン酸成分の合計は、モル比で、１．５〜３．５であり、第２の成分に対する第１の成分の質量比は、０．３５〜０．９の範囲である。【選択図】図１