SLAB CONTINUOUS CASTING METHOD

To inhibit occurrence of longitudinal crack and occurrence of breakout in casting medium-carbon steel.SOLUTION: An electromagnetic stirring device 3 is made to generate an alternate-current moving magnetic field in molten steel existing in a region away by 0.05 m or more and 0.25 m or less from meniscus in a casting mold 1. In the casting mold 1, magnetic flux densities By of the alternate-current moving magnetic field in a region excluding regions m1 and m2 within 100 mm of short side parts 13 and 14 at both ends are set to 0.05 T or more and 0.14 T or less. A number N1 of poles of a first linear motor of the electromagnetic stirring device 3 is set to 5 or more and 6 or less. A number N2 of poles of a second linear motor of the electromagnetic stirring device 3 is set to 5 or more and 6 or less. Phase velocity V represented by the following formula: V=2.f.P is set to 0.3 m/s or more and 1.0 m/s or less, where f is frequencies (Hz) of the alternate-current moving magnetic field and P is pole pitch (m).SELECTED DRAWING: Figure 1 【課題】中炭素鋼の鋳造において、縦割れの発生およびブレークアウトの発生を抑止する。【解決手段】電磁撹拌装置３により、鋳型１内においてメニスカスから０．０５ｍ以上０．２５ｍ以下の領域に存在する溶鋼に、交流移動磁場を発生させる。鋳型１内において、両端の短辺部１３、１４から１００ｍｍ以内の領域ｍ1、ｍ2を除く領域における交流移動磁場の磁束密度Ｂｙを０．０５Ｔ以上０．１４以下とする。電磁撹拌装置３の第１リニアモータのポール数Ｎ1を５以上６以下とする。電磁撹拌装置３の第２リニアモータのポール数Ｎ2を５以上６以下とする。下記式で表される位相速度Ｖを０．３ｍ／ｓ以上１．０ｍ／以下とする。Ｖ＝２・ｆ・Ｐここで、ｆは交流移動磁場の周波数（Ｈｚ）であり、Ｐはポールピッチ（ｍ）である。【選択図】図１