MULTI-LAYER SLIDING BEARING ELEMENT

To provide a sliding bearing element which has a lead-free, sulfur-containing cast alloy layer on a copper basis, and in which the effects of sulfur on the alloy are reduced.SOLUTION: A multi-layer sliding bearing element (1) is provided that contains a supporting metal layer (3), a lead-free copper base alloy layer (4) and a sulfide-containing precipitate (10). The copper base alloy contains 0.1 wt.% to 3 wt.% of sulfur, 0.01 wt.% to 4 wt.% of iron, less than 2 wt.% of phosphorus, 0.1 wt.% to 49 wt.% of the total of at least one element of a first group consisting of zinc, tin, aluminum, manganese, nickel, silicon, chromium and indium, and 0 wt.% to 2 wt.% of the total of at least one element of a second group consisting of silver, magnesium, indium, cobalt, titanium, zirconium, arsenic, lithium, yttrium, calcium, vanadium, molybdenum, tungsten, antimony, selenium, tellurium, bismuth, niobium and palladium, and the balance copper.SELECTED DRAWING: Figure 1 【課題】銅を基材とする無鉛の硫黄含有鋳造用合金有金層を有し、合金に及ぼす硫黄の影響を低減した滑り軸受けエレメントを提供する。【解決手段】支持金属層（３）、無鉛の銅ベース合金層（４）、硫化物含有析出物（１０）を含有し、銅合金が０．１重量％〜３重量％の硫黄、０．０１重量％〜４重量％の鉄、２重量％までのリン、合計で０．１重量％〜４９重量％の亜鉛、錫、アルミニウム、マンガン、ニッケル、ケイ素、クロム、インジウムから成る第１群の少なくとも１種の元素と、合計で０重量％〜２重量％の銀、マグネシウム、インジウム、コバルト、チタン、ジルコニウム、砒素、リチウム、イットリウム、カルシウム、バナジウム、モリブデン、タングステン、アンチモン、セレン、テルル、ビスマス、ニオブ、パラジウムから成る第２群の少なくとも１種とを含有し、残部を銅からなる、多層滑り軸受けエレメント（１）。【選択図】図１