SEPARATOR FILM FOR POWER STORAGE DEVICE AND LITHIUM ION BATTERY INCLUDING THE SAME

To provide a separator film for a power storage device and a lithium ion battery including the same, in which the ion resistance is less likely to increase as compared with a case of a single-layer porous film and the adhesion of a coating film to a resin porous film is high.SOLUTION: A separator film for a power storage device includes a resin porous film, and a coating film formed on one or both sides of the resin porous film, and the coating film is composed of a solid content of an aqueous composition for coating including a binder and a filler, and the binder contains 40 to 45 wt.% of a hydroxyl group-containing monomer unit, 8 to 12 wt.% of an acetyl group-containing monomer, and 50 wt.% or more of water-soluble acrylic resin.SELECTED DRAWING: None 【課題】単層の多孔膜の場合と比較してもイオン抵抗が上がりにくく、コーティング膜の樹脂製多孔フィルムに対する密着性が高い蓄電デバイス用セパレータフィルム及びそれを備えるリチウムイオン電池を提供することを目的とする。【解決手段】樹脂製多孔フィルムと、前記樹脂製多孔フィルムの片面又は両面に形成されたコーティング膜とを含み、前記コーティング膜は、バインダーとフィラーとを含むコーティング用水性組成物の固形分から構成され、前記バインダーは、ヒドロキシル基含有単量体単位を４０〜４５重量％含み、アセチル基含有単量体を８〜１２重量％含む、水溶性アクリル樹脂を５０重量％以上含む、蓄電デバイス用セパレータフィルムによる。【選択図】なし