LASER CLAD LAYER FORMING METHOD AND LASER CLADDING DEVICE

To provide a laser clad layer forming method and a laser cladding device for efficiently forming a laser clad layer of metal with a melting point of 500°C or lower, while preventing a bead from sagging.SOLUTION: Provided is a laser clad layer forming method for forming a laser clad layer of white metal having a melting point of 500°C or lower with respect to the peripheral surface around a central axis C of a base material W. The laser clad layer forming method includes: a molding process S3 in which a planned formation part of a laser clad layer on the peripheral surface of the base material W is irradiated with a laser beam while white metal dust is being fed, so that the dust melts and a bead is molded; and control processes S5-S6 in which the size of a molten pool formed by the laser beam irradiation is controlled during the molding process S3.SELECTED DRAWING: Figure 3 【課題】融点が５００℃以下である金属のレーザクラッド層を、ビードのダレ発生を防止しつつ効率的に形成可能なレーザクラッド層形成方法及びレーザクラッド装置を提供する。【解決手段】レーザクラッド層形成方法は、母材Ｗの中心軸Ｃ周りの周面に対して融点が５００℃以下であるホワイトメタルのレーザクラッド層を形成する方法であって、母材Ｗ周面におけるレーザクラッド層の形成予定部に対して、ホワイトメタル粉末を供給しつつレーザ光を照射し、粉末を溶融させてビードを造形する造形工程Ｓ３と、造形工程Ｓ３の最中に、レーザ光の照射により形成される溶融池の大きさを制御する制御工程Ｓ５〜Ｓ６とを有する。【選択図】図３