MANUFACTURING METHOD OF UNBAKED POLYTETRAFLUOROETHYLENE FILM AND POROUS FILM THEREOF

To provide a manufacturing method of an unbaked PTFE film capable of being continuously formed, and having uniform density distribution and high density, and a manufacturing method of a porous film having no unevenness of thickness and density.SOLUTION: The manufacturing method of an unbaked PTFE film includes filling a mixture by adding a molding assistant to a PTFE fine powder into an extrusion molding mold, and extruding the filled mixture from the extrusion molding mold to prepare an extrusion molded body, rolling the extrusion molded body from a roll to prepare a molding assistant removal film by removing the molding assistant, and reducing thickness of the molding assistant removal film by sandwiching the molding assistant removal film by a nip roll having a rubber roll constituted by coating a metal-made axis core by a rubber under an ordinary temperature and pressing the same to set density at 2.0 g/cmor more.SELECTED DRAWING: None 【課題】本発明は、連続形成が可能であり、密度分布が均一で高密度化された未焼成のＰＴＦＥフィルムの製造方法及び厚み及び密度の斑のない多孔質膜の製造方法を提供することを目的とする。【解決手段】本発明に係る未焼成ＰＴＦＥフィルムの製造方法は、ＰＴＦＥファインパウダーに成形助剤を添加した混合物を押出成形金型に装填し、当該押出成形金型から装填した前記混合物を押し出して押出成形体を作製し、当該押出成形体をロールにより圧延した後に成形助剤を除去した成形助剤除去フィルムを作製し、金属製の軸芯にゴムを被覆して構成されたゴムロールを備えたニップロールにより、常温下において当該成形助剤除去フィルムを挟み込んで圧縮することにより、当該成形助剤除去フィルムの厚みを縮小させて、密度を２．０ｇ／ｃｍ３以上にすることを特徴とする。【選択図】 なし