CEMENT COMPOSITION

To provide a cement composition capable of obtaining a mortar concrete without using a silica fume, the mortar concrete exhibiting low water-binder ratio, high flowability and low viscosity.SOLUTION: A part of a cement in a cement composition is replaced with fly-ash fine particles having particle diameters of 0.2-1.2 μm for a cumulative volume transmission coefficient 25%; particle diameters of 0.3-2.3 μm for a cumulative volume transmission coefficient of 50%; and particle diameters of 0.6-6.0 μm for a cumulative volume transmission coefficient of 90%. The replacement ratio of the fly-ash fine particles to a Portland cement is 10-30 wt.%. Preferably, the fly-ash fine particles to be used has: a Braine's specific surface area of 14,000-42,000 cm/g; and a BET specific surface area of 4-14 m/g.SELECTED DRAWING: None 【課題】シリカヒュームを用いることなく、低水結合材比で高い流動性および低い粘性を示すモルタル・コンクリートを得られるセメント組成物を提供する。【解決手段】セメント組成物のセメントの一部を、累積体積通過率２５％の粒径が０．２〜１．２μｍ、かつ累積体積通過率５０％の粒径が０．３〜２．３μｍ、かつ累積体積通過率９０％の粒径が０．６〜６．０μｍであるフライアッシュ微粉末で置き換える。フライアッシュ微粉末による置換率は、ポルトランドセメントの場合で、１０〜３０重量％とする。使用するフライアッシュ微粉末のブレーン比表面積は１４０００〜４２０００ｃｍ2／ｇ、ＢＥＴ比表面積が４〜１４ｍ２／ｇが好ましい。【選択図】なし