BLACK STAINLESS STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME

To achieve a black stainless steel sheet excellent in corrosion resistance and film adhesion.SOLUTION: An oxide film (L) formed on the surface of a base material (BM) using a stainless steel sheet including Mn:0.04-1.20 mass% and one or more kinds of Ti:0.05-0.50 mass%, Al:0.04-1.00 mass% and Nb:0.05-1.00 mass% as the base material (BM) is a film obtained by laminating a first region (L1) including an internal oxide of one or more of Al, Ti and Mn, a second region (L2) mainly consisting of a Cr oxide and a third region (L3) consisting of a Mn concentrated layer or a Mn and Ti concentrated layer in an order close from the base material (BM). In any cross section of the first region (L1), the internal oxide of one or more of Al, Ti and Mn having a cross sectional area of 0.001 μmor more is distributed by 10 pieces or more per unit area of 1 μmin a range from an interface with the second region (L2) to a depth of 0.5 μm.SELECTED DRAWING: Figure 1 【課題】耐食性および皮膜密着性に優れる黒色ステンレス鋼板を実現する。【解決手段】Ｍｎ：０．０４〜１．２０質量％を含み、さらにＴｉ：０．０５〜０．５０質量％、Ａｌ：０．０４〜１．００質量％、およびＮｂ：０．０５〜１．００質量％のうち１種以上を含むステンレス鋼板を素地（ＢＭ）とし、素地（ＢＭ）の表面に酸化皮膜（Ｌ）が形成されており、酸化皮膜（Ｌ）は、素地（ＢＭ）から近い順に、Ａｌ、Ｔｉ、およびＭｎのいずれか１つ以上の内部酸化物を含む第１領域（Ｌ１）と、主としてＣｒの酸化物からなる第２領域（Ｌ２）と、Ｍｎの濃化層、またはＭｎおよびＴｉの濃化層からなる第３領域（Ｌ３）とが積層された膜であり、第１領域（Ｌ１）の任意の断面において、第２領域（Ｌ２）との界面から深さ０．５μｍまでの範囲に、断面積０．００１μｍ２以上のＡｌ、Ｔｉ、およびＭｎのいずれか１つ以上の内部酸化物が、単位面積１μｍ２あたり１０個以上分布している。【選択図】図１