MANUFACTURING METHOD OF MAGNESIA-SPINEL FIRED BRICK

PROBLEM TO BE SOLVED: To provide a manufacturing method of magnesia-spinel fired brick capable of recycling magnesia/spinel brick after use in a large amount and effectively and capable of maintaining durability by suppressing harmful impurity content.SOLUTION: The manufacturing method of the magnesia-spinel fired brick according to the present invention comprises: blending 10 to 90 mass% of a recycling material of magnesia-spinel fired brick after use or unused with AlOcontent being within a range of 3 to 25 mass% and the porosity being within a range of 10 to 20%, 2 to 8 mass% of an alumina raw material, and a magnesia raw material and/or a spinel raw material as the balance; molding into a predetermined shape the raw material blend obtained with AlOcontent being within a range of 3 to 25 mass%, and the total content of NaO + KO+TiObeing less than 0.5 mass% with respect to 100 mass% of the total content of AlOand MgO; and then firing.SELECTED DRAWING: None 【課題】本発明の目的は、使用後のマグネシア・スピネル質煉瓦を大量且つ有効にリサイクルすることができ、かつ有害な不純物量を抑制することで耐用性を維持することができるマグネシア・スピネル質焼成煉瓦の製造方法を提供することにある。【解決手段】本発明のマグネシア・スピネル質焼成煉瓦の製造方法は、Ａｌ２Ｏ３含有量が３〜２５質量％の範囲内にあり、気孔率が１０〜２０％の範囲内にある使用後または未使用のマグネシア・スピネル質焼成煉瓦のリサイクル原料１０〜９０質量％、アルミナ原料２〜８質量％、及び残部がマグネシア原料および／またはスピネル原料を配合してなり、得られた原料配合物中のＡｌ２Ｏ３含有量が３〜２５質量％の範囲内にあり、且つＡｌ２Ｏ３とＭｇＯの合計含有量１００質量％とした時に、Ｎａ２Ｏ＋Ｋ２Ｏ＋ＴｉＯ２の合計含有量が外掛けで０．５質量％未満である原料配合物を所定の形状に成型した後、焼成することを特徴とする。【選択図】なし