POLYARYLENESULFIDE AND ITS MANUFACTURING METHOD

PROBLEM TO BE SOLVED: To provide a polyarylenesulfide that satisfies all features in which it generates fewer gases during melt-processing, it is excellent in crystallinity, it has high melt crystallization temperature, it has high crystallizing heat quantity, and it is excellent in fluidity, wherein a problem in conventional arts of not obtaining the polyarylenesulfide satisfying these features can be solved.SOLUTION: In a polyarylenesulfide prepolymer, cyclic polyarylenesulfide content is less than 50 wt.%, weight average molecular weight is 2,500 or larger and 20,000 or lower, and oligomer ingredient content is 4 wt.% or lower. This invention relates to a polyarylenesulfide whose: weight average molecular weight is 5,000 or larger and 50,000 or lower; melt crystallization temperature, measured by differential scanning calorimetry, at temperature falling speed of 40°C per minute is 240°C or larger; crystallization heat quantity is more than 55 J/g; and gas yield volatilized when heat-melted for 2 hours at 320°C is 0.2 wt.% or lower, wherein the polyarylenesulfide is provided by (1) heating the polyarylenesulfide prepolymer or by (2) treating the prepolymer with an alkaline earth metal, at temperature range higher than melting temperature of the polyarylenesulfide prepolymer under non-oxidizing atmosphere.SELECTED DRAWING: None 【課題】溶融加工時の発生ガスが少なく、結晶性に優れ溶融結晶化温度が高くかつ結晶化熱量が大きく、流動性に優れるという特性を全て満たすポリアリーレンスルフィドが得られないという従来技術の問題点を解決し、前記した特性を全て満たすポリアリーレンスルフィドを提供することを課題とする。【解決手段】環式ポリアリーレンスルフィド含有量が５０重量％未満であり、重量平均分子量が２，５００以上２０，０００以下であり、オリゴマー成分含有量が４重量％以下であるポリアリーレンスルフィドプレポリマーを、（１）非酸化性雰囲気下においてポリアリーレンスルフィドプレポリマーの融解温度を超える温度範囲で加熱処理および／または（２）アルカリ土類金属処理することにより、重量平均分子量が５，０００以上５０，０００以下のポリアリーレンスルフィドであって、示差走査型熱量計で降温速度４０℃／分の条件にて求めた溶融結晶化温度が２４０℃以上かつ結晶化熱量が５５Ｊ／ｇ以上であり、３２０℃で２時間加熱溶融した際に揮発するガス発生量が０．２重量％以下であるポリアリーレンスルフィドを提供する。【選択図】なし