NEUTRON ABSORBER AND METHOD FOR MANUFACTURING THE SAME

PROBLEM TO BE SOLVED: To obtain a neutron absorber having high neutron absorption power and high fire resistance.SOLUTION: A polymer material used as a base material is a thermosetting polyurethane resin. The thermosetting polyurethane resin is a hard polymer material formed to include a plurality of urethane bonds (-NH CO O-) obtained by reacting a hydroxyl group (-OH) in a polyol compound with an isocyanate group (-NCO) in an isocyanate compound. A boron-containing powder including boron at a high concentration is added to the base material, and the concentration of the boron-containing powder is in a range of 40 to 80 wt.% to the whole. The neutron absorber preferably has an expansion ratio of 1.0 or more and 2.0 or less.SELECTED DRAWING: None 【課題】高い中性子吸収能をもち、かつ耐火性の高い中性子吸収材を得る。【解決手段】母材として用いられる高分子材料は、熱硬化型ポリウレタン樹脂である。この熱硬化型ポリウレタン樹脂は、ポリオール化合物における水酸基（−ＯＨ）と、イソシアネート化合物におけるイソシアネート基（−ＮＣＯ）とが反応することによって、ウレタン結合（−ＮＨ・ＣＯ・Ｏ−）が複数含まれるように形成された硬質の高分子材料である。母材に添加されるのは、ホウ素を高濃度で含有するホウ素含有粉末であり、ホウ素含有粉末の濃度は、全体に対して４０〜８０重量％の範囲である。この中性子吸収材においては、発泡倍率を１．０以上２．０以下とすることが好ましい。【選択図】なし