HARD COAT FILM FOR TRANSFER, HARD COAT LAYER LAMINATE HAVING BASE MATERIAL FILM, AND MANUFACTURING METHOD OF HARD COAT LAYER LAMINATE

PROBLEM TO BE SOLVED: To provide a hard coat film for transfer capable of transferring a hard coat layer onto a resin substrate by thermal transfer, while further improving scratch resistance and weatherability.SOLUTION: A hard coat film for transfer 10 includes at least a hard coat layer 121, a primer layer 122 and an adhesive layer 124 arranged in this order on a base material film 11. The hard coat layer 121 includes a cured product of a curable resin composition containing a curable component and a particle. The curable component includes a bifunctional curable oligomer. The content of the bifunctional curable oligomer is 80 pts.wt. or more with regard to the total mass of the curable component. The content of the particle is over 20 pts.wt. to 150 pts.wt. or less with regard to the total mass of the curable component. The mass ratio is 0.25≤B/A≤1.5 if the bifunctional curable oligomer is A and the particle is B.SELECTED DRAWING: Figure 1 【課題】耐傷性や耐候性をより向上させつつ、樹脂基体上に熱転写によってハードコート層を転写させることの可能な転写用ハードコートフィルムを提供する。【解決手段】この転写用ハードコートフィルム１０は、基材フィルム１１上に、少なくとも、ハードコート層１２１とプライマー層１２２と接着層１２４とがこの順に配置されている。ハードコート層１２１は、硬化性成分と粒子とを含有する硬化性樹脂組成物の硬化物からなる層である。硬化性成分は、２官能の硬化性オリゴマーを含み、２官能の硬化性オリゴマーの含有量は、硬化性成分の総質量に対して８０重量部以上であり、粒子の含有量は、硬化性成分の総質量に対して２０重量部を超え、１５０重量部以下である。また、２官能の硬化性オリゴマーをＡ、粒子をＢとした際の質量比が０．２５≦Ｂ／Ａ≦１．５である。【選択図】図１