MANUFACTURING METHOD OF SINTERING RAW MATERIAL

PROBLEM TO BE SOLVED: To propose a manufacturing method of a sintering raw material capable of suppressing adverse effects due to steel slag while reducing inventory of the steel slag and wet dust by using the steel slag as raw materials of mini-pellets in lieu of dried dust having a less generation amount.SOLUTION: A manufacturing method of a sintering raw material sinters the sintering raw material obtained by mixing mini-pellets having wet dust and dried dust generated in a steel manufacturing process as raw materials into normal raw materials of sintered ore in a Dwight-Lloyd type sintering machine and manufactures the sintered ore for a blast furnace. The mini-pellets are combined with steel slag with a range of more than 0 mass% and equal to 25 mass% or less with respect to total raw materials of the mini-pellets and are granulated. In the manufacturing method of the sintering raw material, it is preferable that the mini-pellets be mixed into the normal raw materials of the sintered ore at any position of a front, an intermediate and a rear of granulation facilities granulating the normal raw material of the sintered ore. 【課題】ミニペレットの原料として、発生量の少ない乾燥ダストに代えて、製鋼スラグを用いることにより、製鋼スラグおよび湿潤ダストの在庫量を削減するとともに、製鋼スラグに起因した弊害を抑止することができる焼結原料の製造方法を提案する。【解決手段】鉄鋼製造過程で発生した湿潤ダストと乾燥ダストを原料とするミニペレットを焼結鉱の通常原料中に混合して得た焼結原料をドワイトロイド式焼結機で焼結して高炉用焼結鉱を製造するときの、上記焼結原料の製造方法であって、上記ミニペレットは、ミニペレットの全原料に対して製鋼スラグを０ｍａｓｓ％超え２５ｍａｓｓ％以下の範囲で配合して造粒したものであり、好ましくは、上記ミニペレットを、焼結鉱の通常原料を造粒する造粒設備の前、中間および後のいずれかの位置で、焼結鉱の通常原料中に混合することを特徴とする焼結原料の製造方法。【選択図】図５