PRODUCTION METHOD OF CELLULOSE ACYLATE FILM, LAMINATE CELLULOSE ACYLATE FILM, POLARIZING PLATE AND LIQUID CRYSTAL DISPLAY DEVICE

PROBLEM TO BE SOLVED: To provide a production method of a cellulose acylate film having excellent productivity of a long film and giving a polarizing plate excellent in durability and contrast property.SOLUTION: The production method of a cellulose acylate film aims to produce a laminate having a three-layer structure composed of a cellulose acylate layer A having an acyl group substitution degree of 2.7 or less and cellulose acylate layers B having an acyl group substitution degree larger than that of the layer A, on either side of the layer A. The method includes: a step (1) of preparing a cellulose acetate resin (a) solution 1 having an acyl group substitution degree of 2.7 or less; a step (2) of preparing a mixture solution 2 of a cellulose acetate resin (b) having an acyl group substitution degree of larger than 2.8 and a cellulose acetate resin (d) having an acyl group substitution degree of 2.7 or less, so as to obtain an acyl group substitution degree of larger than 2.7 in the layer B; and a step (3) of co-flow casing the solution 1 and the solution 2 to produce a film having a dry film thickness of the layer B in the range from 0.5 to 15 μm. 【課題】本発明の課題は、長尺製膜性に優れ、かつ耐久性、コントラスト性に優れる偏光板を与えるセルロースアシレートフィルムの製造方法を提供することにある。【解決手段】本発明のセルロースアシレートフィルムの製造方法は、アシル基置換度が２．７以下のセルロースアシレート層Ａと、層Ａの両側に層Ａのアシル基置換度よりも大なセルロースアシレート層Ｂとからなる３層構成の積層体を有し、アシル基置換度が２．７以下のセルロースアセテート樹脂ａ溶液１を調製する工程（１）、アシル基置換度が２．８より大なセルロースアセテート樹脂ｂと、層Ｂのアシル基置換度が、２．７よりも大となるように、アシル基置換度が２．７以下のセルロースアセテート樹脂ｄの混合溶液２を調製する工程（２）、および該溶液１と該溶液２とを用いて共流延し、該層Ｂの乾燥膜厚を０．５〜１５μｍの範囲内とするフィルムを製造する工程（３）、を有することを特徴とする。【選択図】なし