Thermofusible polymer preform treatment procedure uses ultrasonic vibrations applied along at least one axis to reduce gas/vapour permeability

Treatment procedure comprises subjecting preforms to ultrasonic vibrations along one or more predetermined axes, e.g. in line with and perpendicular to their lengthwise axes, at above 60 deg C. Vibrations are applied at or after injection, but before pre-heating phase prior to blow-moulding, using a sonotrode associated with the preform mould. The treatment procedure for thermofusible polymer preforms consists subjecting them to ultrasonic vibrations along one or more predetermined axes, e.g. in line with and perpendicular to their lengthwise axes, after heating to and maintaining at a temperature of above about 60 deg C. The vibrations are applied at or after the moment of injection, but before the pre-heating phase prior to blow-moulding, using a sonotrode associated with the preform mould, and after vibrating the preforms are cooled to below 60 deg C before pre-heating. L'invention concerne un procédé de traitement de préformes réalisées en un polymère thermofusible injecté, tel que notamment le polyéthylène téréphtalate (PET), ce procédé de traitement étant essentiellement physique et permettant de réduire la perméabilité aux gaz et aux vapeurs des parois des récipients réalisés par soufflage à partir de ces préformes. Il est principalement caractérisé en ce que l'on applique à ces préformes préalablement portées à une température supérieure à 60degreC, des vibrations ultrasoniques selon au moins un axe prédéterminé. L'application de ces vibrations ultrasoniques est faite au moment de l'injection des préformes ou postérieurement à cette injection et ensuite l'on refroidit ces préformes à une température inférieure ou égale à la température ambiante en vue de leur utilisation ultérieure pour la fabrication de récipients par soufflage.