Treatment soln. for bimetallic lithographic printing plates - contg. potassium permanganate nitric acid and phosphoric acid or sulphuric acid

Treatment soln. for polymetallic lithographic plates to give hydrophilic and ink-receptive areas, comprises an aq. soln. contg. 0.5-100 (0.5-3) g/l potassium permanganate; 5-100 (10-30) g/l H3PO4 and/or H2SO4, and 1-20 (2-5) g/l HNO3. The solns. are esp. useful for treatment of polymetallic lithographic plates with a sensitised polyvinyl alcohol (PVA) coating. After exposure, the plates are developed, fixed and etched in the usual way, then the remainder of the PVA layer is removed in a soln. contg. e.g. 5-100 (10-50) g/l Na paraperiodate. The plate is treated with the soln. to form the hydrophilic and ink receptive areas. The treatment solns. give rapid one-stage pretreatment of bimetallic copper-chrome printing plates and simultaneously remove the remainder of the resist layer whilst rendering the copper ink- receptive and the chromium hydrophilic. L'INVENTION CONCERNE UNE SOLUTION DE PREPARATION DES PLAQUES LITHOGRAPHIQUES POLYMETALLIQUES PERMETTANT D'AMELIORER A LA FOIS L'ENCROPHILIE DU CUIVRE ET L'HYDROPHILIE DU CHROME. ELLE EST CONSTITUEE D'UN MELANGE DANS DES PROPORTIONS DEFINIES DE PERMANGANATE DE POTASSIUM, D'ACIDE SULFURIQUE ETOU PHOSPHORIQUE ET D'ACIDE NITRIQUE.EN AJOUTANT DU PERIODATE DE SODIUM A CETTE SOLUTION, ON OBTIENT UNE SOLUTION QUI PERMET DE REALISER A LA FOIS L'INVERSION DE LA PLAQUE, SI CELLE-CI A ETE SENSIBILISEE AVEC DE L'ALCOOL POLYVINYLIQUE, ET LA PREPARATION DES METAUX.L'INVENTION CONCERNE EGALEMENT UN PROCEDE DE MISE EN OEUVRE DESDITES SOLUTIONS DANS LEQUEL, APRES TRAITEMENT, LES PLAQUES SONT GOMMEES A L'AIDE D'UNE SOLUTION AQUEUSE DE GOMME ARABIQUE CONTENANT UN AGENT REDUCTEUR DU MANGANESE.APPLICATION : PREPARATION DES PLAQUES LITHOGRAPHIQUES POLYMETALLIQUES.