Sulphur di:oxide mfr. from sulphur - by melting, vaporisation in bubble layer using oxygen and oxidn. in fluidised bed

mfr. involves melting S, vapourisation in a bubble layer and oxidn. of the S vapour formed. The vapourisation is effected by bubbling O2 through the molten S, whilst oxidn. is carried out in a fluidised bef of inert material. Pref. the O2 is bubbled through the molten S at its b.pt. and vapourisation and oxidn. are carried out at 1-35 atm. Pref. quartz sand, silica gel or aluminosilicate is used as inert material. Up to 100 vol% SO2 can be produced the process is 1.5-3 times more intensive than usual and the effect of high temps. on units of the furnace under high pressure conditions is avoided. LA PRESENTE INVENTION CONCERNE UN PROCEDE DE FABRICATION DE L'ANHYDRIDE SULFUREUX, UTILISE DANS LA PRODUCTION DE L'ACIDE SULFURIQUE ET DANS L'INDUSTRIE DES PATES A PAPIER.LE PROCEDE DE FABRICATION DE L'ANHYDRIDE SULFUREUX CONSISTE EN CE QUE LE SOUFRE EST FONDU ET VAPORISE PAR BARBOTAGE D'OXYGENE A TRAVERS UN BAIN DE SOUFRE FONDU ET QUE LES VAPEURS DU SOUFRE AINSI FORMEES SONT OXYDEES PAR L'OXYGENE DANS UN LIT FLUIDISE EN MATERIAU INERTE. LE PRODUIT VISE OBTENU A UNE CONCENTRATION EN ANHYDRIDE SULFUREUX POUVANT ATTEINDRE 100 EN VOLUME. LE PROCEDE SELON L'INVENTION PERMET DE TRAVAILLER AVEC UN RENDEMENT POUVANT ATTEINDRE 2000 A 3500KG PAR M DE LA SURFACE DE LA COUCHE ET PAR HEURE SOUS DES PRESSIONS DE 1 A 35ATM.