PROCESO PARA PRODUCIR UNA CHAPA O BANDA DE ACERO DE LAMINACION EN FRIO CON UNA BUENA CONFORMABILIDAD

LA INVENCION TRATA DE UN PROCEDIMIENTO PARA PRODUCIR UNA CHAPA O LAMINA DE ACERO ENROLLADA EN FRIO CON BUENA CAPACIDAD DE MOLDEO, EN PARTICULAR CAPACIDAD DE ESTIRAMIENTO PARA FABRICAR PIEZAS A PRESION CON ELEVADA RESISTENCIA A LA ABOLLADURA A PARTIR DE UN ACERO CON LA SIGUIENTE COMPOSICION (EN %): 0,01-0,08 % C, 0,10-0,80 % MN, MAXIMO 0,60 % DE SI, 0,015-0,08 % DE AL, MAXIMO 0,005 % DE N, 0,01-0,04 % DE TI Y/O NB, MAXIMO DE 0,15 % DE CU Y/O V Y/O MI, EL RESTO ES HIERRO PRINCIPALMENTE, CONSISTE EN UN PRECALENTAMIENTO DEL LLANTON FUNDIDO HASTA UNA TEMPERATURA POR ENCIMA DE 1050 °C, ENROLLAMIENTO EN CALIENTE CON UNA TEMPERATURA FINAL POR ENCIMA DE AR 3 HASTA 950 °C, DEVANADO DE LA LAMINA ENROLLADA EN CALIENTE EN EL INTERVALO DE 550 HASTA 750 °C, ENROLLADO EN FRIO CON UN GRADO DE MOLDEO TOTAL DE 40 A 85 %, RECOCIDO RECRISTALIZADOR DE LA LAMINA EN FRIO A UNA TEMPERATURA MINIMA DE 720 °C EN UN HORNO CONTINUO, ENFRIAMIENTO CON 5 A 70 K/S Y FINALMENTE EL ACABADO. PCT No. PCT/EP97/02169 Sec. 371 Date Oct. 27, 1998 Sec. 102(e) Date Oct. 27, 1998 PCT Filed Apr. 26, 1997 PCT Pub. No. WO97/46720 PCT Pub. Date Dec. 11, 1997A method for producing a cold-rolled steel sheet or strip with good formability, especially stretch formability, for making pressings with a high buckling resistance from a steel comprising (in % by mass): 0.01 to 0.08% C, 0.10 to 0.80% Mn, maximum 0.15% Si, 0.015 to 0.08% Al, a maximum 0.005% N, 0.01 to 0.04% Ti and/or Nb, whose contents exceeding the quantity necessary for stoichiometric binding of the nitrogen, ranges from 0.003 to 0.015% Ti or 0.0015 to 0.008% Nb, and a maximum 0.15% in total of one or several elements from the group copper, vanadium, nickel, the remainder being iron, including unavoidable impurities, including a maximum 0.08% P and a maximum 0.02% S, comprises preheating the cast slab to a temperature exceeding 1050 DEG C., hot-rolling at a final temperature ranging from over the Ar3 temperature to 950 DEG C., coiling the hot-rolled strip at a temperature ranging from 550 to 750 DEG C., cold-rolling at a total cold-rolling degree of deformation from 40 to 85%, recrystallization annealing of the cold strip in a continuous furnace at a temperature of at least 720 DEG C., subsequent cooling at 5 to 70 K/s; and skin passing.