PROCEDIMIENTO PARA PRODUCIR ESCAMAS DE YESO A PARTIR DE LA DESULFURACION DE GASES

ESTA INVENCION SE REFIERE A UN PROCESO MEJORADO PARA LA PRODUCCION DE ESCAMAS DE DIHIDRATOS DE SULFATO CALCICO DE YESO A PARTIR DE DIHIDRATOS DE SULFATO CALCICO DE YESO EN POLVO OBTENIDOS DE LA DESULFURIZACION DE GASES DE LA COMBUSTION MEDIANTE EL PROCESO DE LA CALIZA HUMEDA. LAS ESCAMAS TIENEN UN TAMAÑO Y RESISTENCIA SUFICIENTES DE TAL MODO QUE EL DIHIDRATO DE SULFATO CALCICO DE YESO SE PUEDE MANIPULAR Y PROCESAR EN UN EQUIPO CONVENCIONAL NORMALMENTE UTILIZADO POR LOS FABRICANTES DE CARTON DE YESO Y OTROS EN LA INDUSTRIA DE LA CONSTRUCCION. EL DIHIDRATO DE SULFATO CALCICO INTERMEDIO OBTENIDO EN EL PROCESO DE DESULFURIZACION SE DESHIDRATA A DE UN 5 A UN 12% EN PESO APROXIMADAMENTE Y DESPUES SE COMPRIME HASTA FORMAR UNA LAMINA DELGADA BAJO UNA CARGA DE COMPACTACION O COMPRESION CON UNA FUERZA DE 4 A 15 TONELADAS POR PULGADA LINEAL DEL ANCHO DE LA LAMINA. DURANTE LA COMPACTACION SE MANTIENE UNA VELOCIDAD LINEAL DE 0,5 A 2,5 PIES POR SEGUNDO LO QUE PROPORCIONA UN TIEMPO DE DURACION DE LA COMPACTACION DE 0,2 A 1,2 SEGUNDOS APROXIMADAMENTE. DURANTE EL PROCESO DE COMPACTACION SE MANTIENE UNA TEMPERATURA ELEVADA PARA REFORZAR LA REFORMACION DEL TAMAÑO DEL CRISTAL Y LA FORMA DEL DIHIDRATO DE SULFATO CALCICO DE YESO. LA COMBINACION DE LA PRESION Y LA TEMPERATURA EN EL DIHIDRATO DE SULFATO CALCICO DE YESO HUMEDO ALTERA LAS CARACTERISTICAS FISICAS DEL DIHIDRATO DE SULFATO CALCICO DE YESO, LO QUE DA COMO RESULTADO UNA LAMINA QUE SE ROMPE FORMANDO ESCAMAS DURAS AL SALIR DE LA ZONA DE COMPACTACION. This invention relates to an improved process for producing gypsum calcium sulfate dihydrate flakes from powdered gypsum calcium sulfate dihydrate obtained from the desulfurization of flue gas by the wet limestone process. The flakes have sufficient size and strength such that the gypsum calcium sulfate dihydrate can be handled and processed in conventional equipment commonly used by wallboard manufacturers and others in the construction industry. The intermediate calcium sulfate dihydrate from the desulfurization process is dewatered to about 5 to 12% by weight and then compressed into a thin sheet under a compaction or compression load of 4 tons force to 15 tons force per linear inch of sheet width. A linear speed of from 0.5 to 2.5 feet per second is maintained during compaction providing a compaction residence time of from about 0.2 to 1.2 seconds. An elevated temperature is maintained during the compaction process to enhance the reformation of the crystal size and shape