Ni-BASED ALLOY HAVING EXCELLENT HIGH-TEMPERATURE CREEP CHARACTERISTICS, AND GAS TURBINE MEMBER USING SAME

Provided is a Ni-based alloy having a composition consisting of, by mass%, Cr: 14.0% to 17.0% (preferably, not less than 14.0% and less than 15.0%), Fe: 5.0% to 9.0%, Ti: 2.2% to 2.8%, Al: 0.40% to 1.00%, a total amount of Nb + Ta: 0.7% to 1.2%, B: 0.001% to 0.010%, Zr: 0.01% to 0.15%, Mg: 0.001% to...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	KOMATSU, Akihiro, SUGAHARA, Katsuo
Format:	Patent
Sprache:	eng ; fre ; ger
Schlagworte:	AIR INTAKES FOR JET-PROPULSION PLANTS ALLOYS BLASTING CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS CHEMISTRY COMBUSTION ENGINES CONTROLLING FUEL SUPPLY IN AIR-BREATHING JET-PROPULSION PLANTS ENGINE PLANTS IN GENERAL FERROUS OR NON-FERROUS ALLOYS GAS-TURBINE PLANTS HEATING HOT-GAS OR COMBUSTION-PRODUCT ENGINE PLANTS INDEXING SCHEME FOR ASPECTS RELATING TONON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES ORJET-PROPULSION PLANTS INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUSSUBCLASSES OF CLASSES F01-F04 LIGHTING MACHINES OR ENGINES IN GENERAL MECHANICAL ENGINEERING METALLURGY NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAMTURBINES STEAM ENGINES TREATMENT OF ALLOYS OR NON-FERROUS METALS WEAPONS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	Provided is a Ni-based alloy having a composition consisting of, by mass%, Cr: 14.0% to 17.0% (preferably, not less than 14.0% and less than 15.0%), Fe: 5.0% to 9.0%, Ti: 2.2% to 2.8%, Al: 0.40% to 1.00%, a total amount of Nb + Ta: 0.7% to 1.2%, B: 0.001% to 0.010%, Zr: 0.01% to 0.15%, Mg: 0.001% to 0.050%, Mn: 0.01% to 0.20%, Cu: 0.005% to 0.300%, Mo: 0.01% to 0.30%, C: 0.01% to 0.05%, and the balance of Ni with inevitable impurities. In a creep test under conditions of a test temperature of 750°C and a test load of 330 MPa, the Ni-based alloy preferably has a creep rupture life of not less than 120 hours and an elongation of not less than 16%, i.e., has good high-temperature creep characteristics. The Ni-based alloy is suitable for a gas turbine member.