Method for producing a flat steel product with high reflection capacity, flat steel product, and mirror element for solar concentrators

The method involves providing a steel flat product with an upper surface of an arithmetical middle rough value smaller than a micro meter. The resulted steel product is annealed under an inert gas atmosphere with hydrogen content of more than 50 volume percent. A dry performance-forming re-rolling of the annealed steel flat product is dry performance-forming re-rolled with post-rolling degree of 0.5 to 2 percentages. A coating of the flat steel product is selectively determined at a terminal in re-rolled condition with a reflective coating. Independent claims are also included for the following: (1) a steel flat product (2) a mirror element for a solar concentrator. Die Erfindung betrifft ein Verfahren zum Herstellen eines Stahlflachprodukts mit hohem Reflektionsvermögen, dessen Oberflächen einen arithmetischen Mittenrauwert Ra von weniger als 0,03 µm aufweisen und bei dem Stahlflachprodukt, das an mindestens einer Oberfläche einen arithmetischen Mittenrauwert Ra < 2,5 µm aufweist, in mehreren Walzstichen kaltgewalzt wird, die über das Kaltwalzen erzielte Gesamtverformungsrate 75 - 90 % beträgt, die Verformungsrate von Walzstich zu Walzstich abnimmt, der Walzdruck im ersten Walzstich 200 - 800 MPa und der Walzdruck im letzten Walzstich 1000 - 4000 MPa beträgt, das Kaltwalzen unter Zugabe eines Walzöls mit einer Viskosität 5 - 10 mm 2 /s bei 40 °C erfolgt, die Walzgeschwindigkeit > 200 m/min ist und das Kaltwalzen mindestens im letzten Walzstich mit einer Arbeitswalze erfolgt, die einen Mittenrauwert Ra < 0,01 µm aufweist. Anschließend wird das kaltgewalzte Stahlflachprodukt unter einer Schutzgasatmosphäre geglüht und trocken nachgewalzt. Die Erfindung betrifft auch ein entsprechend erzeugtes Stahlflachprodukt und einen Solarkonzentrator, hergestellt aus einem solchen Stahlflachprodukt.