JET PUMP BEAM AND METHOD FOR PRODUCING THE SAME

A jet pump beam is made of improved heat-treated precipitation-hardened nickel base alloy excellent in anti-stress corrosion cracking properties and high-temperature strength, and having high ductility and a high elastic modulus. A jet pump beam 27 made of improved heat-treated nickel base alloy is produced by preparing a precipitation-strengthened nickel base alloy material having a component composition containing by mass%, Ni: 50.0% to 55.0%, Cr: 17.0% to 21.0%, Nb+Ta: 4.75% to 5.50%, Mo: 2.8% to 3.3%, Ti: 0.65% to 1.15%, Al: 0.2% to 0.8%, C: 0.08% or less, Mn: 0.35% or less, Si: 0.35% or less, S: 0.015% or less, P: 0.03% or less, Cu: 0.30% or less, B: 0.006% or less, and Co: 1.0% or less, and Fe and inevitable impurities constituting a remaining part, subjecting the nickel base alloy material to solution heat treatment at a temperature of 1010°C to 1090°C, and subjecting the nickel base alloy material to age-hardening heat treatment at a temperature of 694°C to 714°C for 5 to 7 hours after the solution heat treatment.