MOLDABLE POLYESTER COMPOSITIONS, PROCESSES OF MANUFACTURE, AND ARTICLES THEREOF

A thermoplastic composition comprises, based on the total weight of the composition: 51-90 wt % polyester, 10-49 wt % ABS impact modifier; 0-20 wt % of multifunctional epoxy compound; 0-40 wt % filler; 0-2 wt % fibrillated fluoropolymer; and more than 0 to 5 wt % of a stabilizer composition. An arti...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	AGARWAL, PARAMINDER, JUIKAR, VISHVAJIT CHANDRAKANT, ELLINGTON, DONALD HOWARD, MILLER, KENNETH FREDERICK, GALLUCCI, ROBERT RUSSELL, SRINIVASAN, VEERARAGHAVAN, ODEH, IHAB, VAN GISBERGEN, JOSEPHUS GERARDUS M, RANGANATHAN, SATHIS KUMAR
Format:	Patent
Sprache:	eng ; fre ; ger
Schlagworte:	AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING CHEMISTRY COMPOSITIONS BASED THEREON COMPOSITIONS OF MACROMOLECULAR COMPOUNDS METALLURGY ORGANIC MACROMOLECULAR COMPOUNDS PERFORMING OPERATIONS SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDEDFOR SHAPING OR JOINING OF PLASTICS THEIR PREPARATION OR CHEMICAL WORKING-UP TRANSPORTING USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES ASCOMPOUNDING INGREDIENTS WORKING OF PLASTICS WORKING OF SUBSTANCES IN A PLASTIC STATE, IN GENERAL
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	A thermoplastic composition comprises, based on the total weight of the composition: 51-90 wt % polyester, 10-49 wt % ABS impact modifier; 0-20 wt % of multifunctional epoxy compound; 0-40 wt % filler; 0-2 wt % fibrillated fluoropolymer; and more than 0 to 5 wt % of a stabilizer composition. An article blow molded or injection molded from the composition has a multi-axial impact total energy from 30-100 Joules at −30° C. and a ductility of more than 90%; a permeability of more than 0 and less than or equal to 1.5 g/m2-day to ASTM D 471-98 Fuel C, measured after exposure to ASTM D 471-98 Fuel C vapor for 20 weeks at 40° C.; an MVR of 1-20 cc/10 min., measured at 265° C.; a flexural modulus of greater than 1300 MPa; and retains at least 75% of its initial tensile elongation at break, after exposure to Fuel E85 for 28 days at 70° C.