Fire-resistant welding steel in the form of hollow profiles, supports or molded steel contains alloying additions of silicon, manganese, aluminum, molybdenum, tungsten and niobium

Fire-resistant welding steel in the form of hollow profiles, supports or molded steel contains (in wt.%) 0.06-0.13 C, 0.15-0.50 Si, 1.0-2.0 Mn, maximum 0.025 P, maximum 0.02 S, 0.005-0.040 Al, 0.20-0.40 Mo, 0.40-0.70 W, 0.02-0.05 Nb and a balance of Fe with unavoidable impurities. A component made from the steel has a yield point at elevated temperature of at least 200 MPa at 600[deg] C and a CEIIW value of less than 0.5. An independent claim is also included for a process for the production of hot-rolled hollow profiles having a thickness of up to 30 mm made from the above steel comprising casting the steel into strands, hot rolling into rods and then into hollow profiles at at least 1200[deg] C before cooling in air. Die Erfindung betrifft einen feuerresistenten schweißbaren Stahl, insbesondere in Form von warmgewalzten Hohlprofilen, Trägern, Formstahl oder Grobblech für den Stahlbau mit folgender chemischer Zusammensetzung (in Masse-%): DOLLAR A 0,06-0,13% C DOLLAR A 0,15-0,50% Si DOLLAR A 1,0-2,0% Mn DOLLAR A max. 0,025% P DOLLAR A max. 0,02% S DOLLAR A 0,005-0,040% Al DOLLAR A 0,20-0,40% Mo DOLLAR A 0,40-0,70% W DOLLAR A 0,02-0,05% Nb DOLLAR A Rest Eisen mit erschmelzungsbedingten Verunreinigungen, wobei das aus diesem Stahl hergestellte Bauteil eine Warmstreckgrenze bei 600 DEG C von mindestens 200 MPa und einen CE¶IIW¶-Wert < 0,5 aufweist. DOLLAR A Ferner betrifft die Erfindung ein Verfahren zur Herstellung von Hohlprofilen und von Trägern oder Formstahl aus diesem Stahl.