Thermoplastic resin composition for use in producing injection-molded article, comprises polypropylene resin, elastomer, inorganic filler, and resin

A thermoplastic resin composition comprises 35-85 wt.% polypropylene resin, 10-35 wt.% elastomer, 2-30 wt.% inorganic filler, and 5-15 wt.% resin. The resin has a melt tension at winding speed of 15.7 m/min, of 0.03-0.1 N, and swelling ratio of \-0.8 at 220 deg C. A thermoplastic resin composition comprises 35-85 wt.% polypropylene resin, 10-35 wt.% elastomer, 2-30 wt.% inorganic filler, and 5-15 wt.% resin. The resin has a melt tension at winding speed of 15.7 m/min, of 0.03-0.1 N, and swelling ratio of \-0.8 at 220 deg C, L/D of an orifice of 40 and shear rate of 1.2 asterisk 10 /sec. The time required for the resin until the ratio of relaxation elastic modulus at 210 deg C and relaxation elastic modulus at 0.02 second reaches 0.01 is 5-10 seconds. Offenbart wird eine thermoplastische Harzzusammensetzung, umfassend (A) 35 bis 85 Gew.-% eines Polypropylenharzes, (B) 10 bis 35 Gew.-% eines Elastomers, (C) 2 bis 30 Gew.-% eines anorganischen Füllstoffes und (D) 5 bis 15 Gew.-% eines Harzes, wobei das Harz (D) eine Schmelzspannung (MT), gemessen bei einer Drehgeschwindigkeit von 15,7 m/min, von nicht niedriger als 0,03 N und niedriger als 0,1 N und ein Quellverhältnis (SR), gemessen bei 220 DEG C, einem L/D einer Auslassöffnung von 40 und einer Scherrate von 1,2 x 10·3· s·-1·, von 1,8 oder mehr hat, und die Zeit, die das Harz (D) benötigt, bis das Verhältnis (G(t)/G(0,02)) des Relaxationselastizitätsmoduls G(t), gemessen bei 210 DEG C, zum Relaxationselastizitätsmodul G(0,02) bei einer Zeit von 0,02 Sekunden, 0,01 erreicht, nicht niedriger als 5 Sekunden und niedriger als 10 Sekunden ist.