Verfahren zur Herstellung von Titandioxid und das so erhaltene Titandioxid

Die Erfindung betrifft ein Verfahren zur Herstellung von Titandioxid mit einem Anteil von höchstens 10% (numerisch) an Kristalliten mit einer Größe von unter 100 nm sowie das nach diesem Verfahren erhaltene Titandioxid. A process for producing a particulate TiO2 includes supplementing metatitanic acid with an alkali compound in a quantity of 1200 ppm to 2400 ppm of alkali, with a phosphorus compound in a quantity of 0.1 wt.-% to 0.3 wt.-% by weight of P, expressed as phosphorus, and with an aluminum compound in a quantity of 1 ppm to 1000 ppm of Al, expressed as Al, to obtain a mixture. The quantity of the alkali compound, of the phosphorus compound, and of the aluminum compound are with respect to the TiO2 content. The mixture is calcined at a constant temperature of 940° C. to 1020° C. until a numerical fraction X50 of TiO2 has a primary crystallite size of at least 200 nm, to obtain a calcined mixture. The calcined mixture is cooled to obtain a cooled calcined mixture. The cooled calcined mixture is grinded to obtain the particulate TiO2.