LAMINATE, METHOD FOR MANUFACTURING LAMINATE, OPTICAL MEMBER, OPTICAL DEVICE, METHOD FOR MANUFACTURING OPTICAL MEMBER, AND METHOD FOR MANUFACTURING OPTICAL DEVICE

The purpose of the present invention is to provide a laminate of a void layer and an adhesive layer, said laminate having both adhesive force or adhesive force and difficulty in penetration of an adhesive or an adhesive into voids. In order to achieve the purpose, this laminate (10) or (10a) is obta...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	HAMADA CHIE, SUGINO AKIKO, YOSHIMI TOSHIYA
Format:	Patent
Sprache:	chi ; eng
Schlagworte:	ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE ADHESIVES CHEMICAL PAINT OR INK REMOVERS CHEMISTRY COATING COMPOSITIONS, e.g. PAINTS, VARNISHES ORLACQUERS CORRECTING FLUIDS DYES FILLING PASTES INKS LAYERED PRODUCTS LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT ORNON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM METALLURGY MISCELLANEOUS APPLICATIONS OF MATERIALS MISCELLANEOUS COMPOSITIONS NATURAL RESINS NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL PAINTS PASTES OR SOLIDS FOR COLOURING OR PRINTING PERFORMING OPERATIONS POLISHES TRANSPORTING USE OF MATERIALS AS ADHESIVES USE OF MATERIALS THEREFOR WOODSTAINS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The purpose of the present invention is to provide a laminate of a void layer and an adhesive layer, said laminate having both adhesive force or adhesive force and difficulty in penetration of an adhesive or an adhesive into voids. In order to achieve the purpose, this laminate (10) or (10a) is obtained by laminating a void layer (11), an intermediate layer (12), and an adhesive layer (13) in this order, and the intermediate layer (12) is a layer containing a polymer having a glass transition temperature (Tg) of 30 DEG C or more. 本发明的目的在于提供兼顾粘合力或粘接力、和粘合剂或粘接剂向空隙的浸透困难性的空隙层与粘合粘接层的层叠体。为了实现上述目的，本发明的层叠体(10)或(10a)依次层叠有空隙层(11)、中间层(12)及粘合粘接层(13)，中间层(12)是包含玻璃化转变温度(Tg)为30℃以上的聚合物的层。