Preparation process of PEDOT: PSS electron-ion mixed flexible thermoelectric thin film

The invention provides a PEDOT: PSS electron ion mixed flexible thermoelectric film preparation process, which is characterized by comprising the following steps: dissolving 7g of AAM in 4mL of deionized water, and carrying out ultrasonic dispersion for 5 minutes; 7 mg of MAA is added into the solution to be mixed, and mixing is conducted for 30 min at the speed of 800 r/min; 0.015 g of MBAAM and 110 mg of APS are slowly added into the AAM solution, and dispersion is carried out for 10 min; 0.25 g of a PEDOT: PSS solution (the solid content is 1.0%-1.3%) is added into the mixed solution, and a uniformly mixed solution is obtained; casting the mixed solution into a mold (100mm * 100mm * 10mm), placing the mold in a drying oven, and reacting at 65 DEG C for 2 hours; the PEDOT: PSS/P (AAM-MAA) electron ion mixed flexible thermoelectric thin film prepared by the method has the advantages of high power generation power, good flexibility, impact resistance and free bending. 本发明提出了一种PEDOT：PSS电子离子混合型柔性热电薄膜制备工艺，其特征在于，